LINCORE® 102W (SAW) Metal-Cored Submerged Arc Wire produces a tool steel deposit that retains hardness at high working temperatures. Recommended primary 802 and secondary 860 standard flux are not sized for semiautomatic applications; however, they can be ordered in special sizing by contacting your Lincoln Electric representative
Features
- Metal-cored wire which produces a tool steel deposit that retains hardness at high working temperatures
- Excellent material for severe abrasion applications
- Resistance to abrasion is 50 to 60 times that of plain carbon steel
Disclaimers
Service Information
You May Also Need
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
MECHANICAL PROPERTIES
| Flux | Classification | Hardness Rockwell C |
|---|---|---|
| Lincolnweld® 802® | Typical Result | 48-54 |
DEPOSIT COMPOSITION
| Flux | Classification | %C | %Cr | %Mn | %Mo | %Si | %V | %W |
|---|---|---|---|---|---|---|---|---|
| Lincolnweld® 802® | Typical Result | 0.28 | 6.5 | 1.5 | 1.0 | 0.4 | 0.15 | 1.0 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
|---|---|---|---|---|
| 3/32 in (2.4 mm) | DC+ | 1.7 (65) | 24 | 240 |
| 3/32 in (2.4 mm) | DC+ | 3.0 (120) | 28 | 400 |
| 3/32 in (2.4 mm) | DC+ | 4.4 (175) | 31 | 500 |
| 1/8 in (3.2 mm) | DC+ | 1.5 (60) | 26 | 390 |
| 1/8 in (3.2 mm) | DC+ | 2.5 (100) | 28 | 540 |
| 1/8 in (3.2 mm) | DC+ | 3.6 (140) | 30 | 680 |
| 5/32 in (4.0 mm) | DC+ | 1.4 (55) | 27 | 500 |
| 5/32 in (4.0 mm) | DC+ | 2.2 (85) | 30 | 685 |
| 5/32 in (4.0 mm) | DC+ | 2.9 (115) | 32 | 850 |