Lincore® 33

Flux-Cored Self-Shielded (FCAW-S)

Ideal for building up on carbon and low alloy steels. Use as an underbase for carbon steel parts prior to hardfacing.

DETAILS

Ideal for building up on carbon and low alloy steels. Use as an underbase for carbon steel parts prior to hardfacing. Great compressive strength under heavy loading. Deposits are generally crack free, machinable and can be flame cut. Deposit thickness is unlimited.

Features

  • Build-up deposit on carbon steel and low alloy steel base metals
  • Unlimited layers
  • Delivers tough machinable deposits for build-up or final overlay intended for metal-to-metal wear

Typical Applications

  • Build-up deposit on carbon steel and low alloy steel base metals

Welding Positions

  • Flat/Horizontal

Disclaimers

Warning -

Cancer and Reproductive Harm -

www.P65Warnings.ca.gov

Service Information

Documentation

You May Also Need

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

MECHANICAL PROPERTIES

Classification Number of layer Hardness Rockwell C
Typical Result 1 Layer 14-30
Typical Result 2 Layers 26-32
Typical Result 3 Layers 25-34
Typical Result, Work-hardened 1 Layer 28-34
Typical Result, Work-hardened 2 Layers 32-36
Typical Result, Work-hardened 3 Layers 35-38
Typical Result, Flame-hardened 2 Layers 38-42

DEPOSIT COMPOSITION

Classification Product Size %Al %C %Cr %Mn %P %S %Si
Typical Result .045" (1.1 mm) 1.6-1.9 0.11-0.18 1.2-1.4 1.8-2.1 0.004-0.012 0.002-0.005 0.50-0.75
Typical Result 1/16" (1.6 mm) 1.6-1.9 0.11-0.18 1.2-1.4 1.8-2.1 0.004-0.012 0.002-0.005 0.50-0.75
Typical Result 5/64" (2.0 mm) 1.4-1.7 0.13-0.15 1.1-1.4 2.1-2.3 0.004-0.008 0.002-0.005 0.45-0.60
Typical Result 7/64" (2.8 mm) 1.4-1.7 0.13-0.15 1.1-1.4 2.1-2.3 0.004-0.008 0.002-0.005 0.45-0.60

TYPICAL OPERATING PROCEDURES

Diameter Polarity ESO
mm (in.)
Wire Feed Speed
m/min (in/min)
Voltage
volts
Approx. Current
amps
Deposition Rate
kg/hr (lb/hr)
0.045 in (1.1 mm) DC+ 45 (1 3/4) 5.1 (200) 25 80 1.5 (3.3)
0.045 in (1.1 mm) DC+ 45 (1 3/4) 8.9 (350) 28 130 2.7 (6.0)
0.045 in (1.1 mm) DC+ 45 (1 3/4) 12.7 (500) 31 150 3.9 (8.7)
1/16 in (1.6 mm) DC+ 45 (1 3/4) 3.8 (150) 26 125 2.1 (4.6)
1/16 in (1.6 mm) DC+ 45 (1 3/4) 6.4 (250) 29 180 3.5 (7.8)
1/16 in (1.6 mm) DC+ 45 (1 3/4) 8.9 (350) 32 225 5.0 (11.1)
5/64 in (2.0 mm) DC+ 50 (2) 3.2 (125) 23 200 3.1 (6.9)
5/64 in (2.0 mm) DC+ 50 (2) 5.1 (200) 27 290 4.9 (10.8)
5/64 in (2.0 mm) DC+ 50 (2) 6.4 (250) 29 325 6.1 (21.1)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 3.4 (135) 26 360 5.7 (12.6)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 4.4 (175) 28 420 7.3 (16.0)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 6.0 (235) 30 470 9.6 (21.1)