33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Diameters / Packaging

Diameters
 11.3 KG SPOOL
0.045 in (1.1 mm) ED031120
5/64 in (2.0 mm) ED031122

Lincore® 55

Metal-Cored Submerged Arc (SAW) | ED031121

CLASSIFICATIONS:
EN ISO : T Fe2

Low Alloy steels designed for rebuilding of carbon or low alloy parts used in Metal-to-Metal wear applications, works best in non-lubricated rolling or sliding

Diameter

Select Diameter

  • 0.045 in (1.1 mm)
  • 5/64 in (2.0 mm)

Package

Select Package

  • 11.3 KG SPOOL

This product could be discontinued. Please contact Customer Service.

DETAILS

Ideal for building up on carbon and low alloy steels. Use as an underbase for carbon steel parts prior to hardfacing. Great compressive strength under heavy loading. Deposits are generally crack free, machinable and can be flame cut. Deposit thickness is unlimited. Used in Metal-to-Metal wear applications, works best in non-lubricated rolling or sliding.

Features

  • To be used on carbon steel, low alloy steel and manganese steel
  • Unlimited layers with proper preheat and interpass temperatures and procedures
  • Delivers a deposit which resists metal-to-metal rolling or sliding wear as well as mild abrasion

Service Information

Documentation

You May Also Need

33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Lincore® 55

ED031120
33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Lincore® 55

ED031122

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

MECHANICAL PROPERTIES

Classification Number of layer Hardness Rockwell C
Typical Result 1 Layer 50-59
Typical Result 2 Layers 50-60
Typical Result, Work-hardened 1 Layer 53-62
Typical Result, Work-hardened 2 Layers 56-62
Typical Result, Flame-hardened 2 Layers 52-54
Typical Result, 180°C (350°F) Interpass Temp 1 Layer 50-55
Typical Result, 180°C (350°F) Interpass Temp 2 Layers 55-59

DEPOSIT COMPOSITION

Classification Product Size %Al %C %Cr %Mn %Mo %P %S %Si
Typical Result .045" (1.1 mm) 1.4 0.45 5.3 1.3 0.8 0.010 0.004 0.53
Typical Result 1/16" (1.6 mm) 1.4 0.45 5.3 1.3 0.8 0.010 0.004 0.53
Typical Result 5/64" (2.0 mm) 1.4 0.45 5.3 1.4 0.8 0.010 0.004 0.60
Typical Result 7/64" (2.8 mm) 1.4 0.45 5.3 1.4 0.8 0.010 0.004 0.60

TYPICAL OPERATING PROCEDURES

Diameter Polarity ESO
mm (in.) 		Wire Feed Speed
m/min (in/min) 		Voltage
volts 		Approx. Current
amps 		Deposition Rate
kg/hr (lb/hr)
0.045 in (1.1 mm) DC+ 45 (1 3/4) 5.1 (200) 25 85 1.6 (3.6)
0.045 in (1.1 mm) DC+ 45 (1 3/4) 8.9 (350) 28 125 3.0 (6.6)
0.045 in (1.1 mm) DC+ 45 (1 3/4) 12.7 (500) 31 165 4.3 (9.4)
1/16 in (1.6 mm) DC+ 45 (1 3/4) 3.8 (150) 26 125 2.2 (4.8)
1/16 in (1.6 mm) DC+ 45 (1 3/4) 6.4 (250) 29 195 3.8 (8.4)
1/16 in (1.6 mm) DC+ 45 (1 3/4) 8.9 (350) 32 245 5.5 (12.1)
5/64 in (2.0 mm) DC+ 45 (1 3/4) 3.2 (125) 24 190 3.2 (7.0)
5/64 in (2.0 mm) DC+ 45 (1 3/4) 5.1 (200) 27 295 5.0 (11.0)
5/64 in (2.0 mm) DC+ 45 (1 3/4) 6.4 (250) 30 330 6.2 (13.7)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 2.3 (90) 25 280 3.8 (8.4)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 3.2 (125) 27 350 5.2 (11.5)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 4.4 (175) 30 420 7.3 (16.0)

NOTES

Note
Cold parts should be warmed to at least 25°C (75°F). Higher preheat of 150 - 260°C (300 - 500°F) may be necessary on thick parts or heavy sections.
Interpass temperatures between 150°C (300°F) and 200°C (400°F) do not affect the hardness of Lincore® 55 significantly.