Lincore® 60-O

Flux-Cored Self-Shielded (FCAW-S)

Iron-based with a large amount of chromium carbides in a hard matrix. Severe Abrasion with Low Impact

DETAILS

Iron-based with a large amount of chromium carbides in a hard matrix. These alloys are designed for severe sliding abrasion accompanied by low or moderate impact.

Features

  • To be used on carbon, low alloy, manganese and stainless steels and cast iron
  • Deposit is limited to two layers
  • Deposits feature higher alloy levels than to resist both abrasion and moderate impact

Typical Applications

  • Bucket lips
  • Crusher hammers
  • Ore chutes
  • Dozer blades
  • Ripper Teeth

Welding Positions

  • Flat/Horizontal

Disclaimers

Warning -

Cancer and Reproductive Harm -

www.P65Warnings.ca.gov

Service Information

You May Also Need

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

MECHANICAL PROPERTIES

Classification Number of layer Hardness Rockwell C Mass Loss (G65)
Typical Result 1 Layer 50-55 0.67
Typical Result 2 Layers 55-58 0.20

DEPOSIT COMPOSITION

Classification Number of layer %Al %C %Cr %Mn %Si
Typical Result 2 Layers 0.3-0.4 4.0-4.6 18.5-22.9 1.0-1.8 0.5-0.9

TYPICAL OPERATING PROCEDURES

Diameter Polarity ESO
mm (in.)
Wire Feed Speed
m/min (in/min)
Voltage
volts
Approx. Current
amps
Deposition Rate
kg/hr (lb/hr)
.045" (1.1 mm) DC+ 19 (1) 5.1 (200) 21 125 1.9 (4.1)
.045" (1.1 mm) DC+ 19 (1) 10.2 (400) 25 185 3.7 (8.2)
.045" (1.1 mm) DC+ 19 (1) 12.7 (500) 27 210 4.7 (10.3)
1/16" (1.6 mm) DC+ 22 (1) 5.1 (200) 28 240 3.4 (7.6)
1/16" (1.6 mm) DC+ 22 (1) 7.6 (300) 31 300 5.1 (11.2)
1/16" (1.6 mm) DC+ 22 (1) 11.4 (450) 33 350 7.5 (16.6)
5/64" (2.0 mm) DC+ 32 (1) 3.2 (125) 26 250 3.4 (7.4)
5/64" (2.0 mm) DC+ 32 (1) 5.1 (200) 30 350 5.4 (12.0)
5/64" (2.0 mm) DC+ 32 (1) 6.4 (250) 32 400 6.8 (15.1)
7/64" (2.8 mm) DC+ 29 (1) 1.9 (75) 27 250 3.4 (7.4)
7/64" (2.8 mm) DC+ 29 (1) 3.2 (125) 30 340 5.4 (11.9)
7/64" (2.8 mm) DC+ 29 (1) 4.4 (175) 32 420 7.5 (16.5)

NOTES

Note
Deposit thickness limit is two layers unless high travel speed is used to obtain very closely spaced check cracks. Many layers can be used with high travel speed and small bead sizes to ensure close-spaced check cracks.
Lincore® 60-O deposit cross cracks (commonly called cross-checking) on cooling. This is desirable, since cross-cracking of the deposit relieves cooling stresses and prevents spalling.