Lincoln® SHS® 7570W

SHS®7570W coatings exhibit excellent corrosion resistance, high wear resistance, high impact resistance and superior bond strength. Superior bond strength values of these coatings signify that this material has exceptional adhesion and cohesion. High adhesion values highlight the extremely low residual stress (even at high thicknesses) that is an inherent factor in this coating type. High cohesion values mean that the probability of “pull-out” of individual particles is extremely low during wear, erosion and other service conditions. Low porosity means low coating permeability, resulting in a highly corrosion resistant barrier. Low oxide content is another key ingredient contributing to the high bond strength of SHS®7570W due to the very limited presence of internal voids and other defects. These characteristics provide predictable coating performance across a broad variety of service environments. SHS®7570W develops extreme passive film stability at a range of pH in both oxidizing and reducing environments. SHS®7570W is especially resistant to corrosion in high chlorine and seawater environments, making it a viable alternative that offers significantly better wear performance than nickel superalloys and stainless steels.

Features

• Excellent corrosion resistance and high wear and impact resistance
• Especially resistant to corrosion in high chloride and seawater
• Alternative to nickel and superalloys and stainless steels

Typical Applications

• Oil & Gas
• Power Generation
• Pulp & Paper

Welding Positions

• Flat/Horizontal