Lincore® 410NiMo

Submerged Arc (SAW) | ED018590

Low Alloy steels designed for rebuilding of carbon or low alloy parts used in Metal-to-Metal wear applications, works best in non-lubricated rolling or sliding

DETAILS

Ideal for building up on carbon and low alloy steels. Use as an underbase for carbon steel parts prior to hardfacing. Great compressive strength under heavy loading. Deposits are generally crack free, machinable and can be flame cut. Deposit thickness is unlimited. Used in Metal-to-Metal wear applications, works best in non-lubricated rolling or sliding.

Features

  • Use on low alloy steels
  • Deposit is unlimited layers
  • Metal-cored wire with low carbon deposit, which forms softer, tougher martensite than other roll alloys
  • Works well with Lincolnlweld 801 Flux or Lincolnlweld 802 Flux

Disclaimers

Warning -

Cancer and Reproductive Harm -

www.P65Warnings.ca.gov

You May Also Need

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

MECHANICAL PROPERTIES

Flux Classification Hardness Rockwell C
Lincolnweld® 801® Typical Result 32-40

DEPOSIT COMPOSITION

Flux Classification %C %Cr %Mn %Mo %Ni %Si
Lincolnweld® 801® Typical Result 0.05 13.0 0.8 1.0 2.0 0.5

TYPICAL OPERATING PROCEDURES

Diameter Polarity Wire Feed Speed
m/min (in/min)
Voltage
volts
Approx. Current
amps
3/32 in (2.4 mm) DC+ 1.7 (65) 24 250
3/32 in (2.4 mm) DC+ 3.0 (120) 28 325
3/32 in (2.4 mm) DC+ 4.4 (175) 31 425
1/8 in (3.2 mm) DC+ 1.5 (60) 26 325
1/8 in (3.2 mm) DC+ 3.6 (140) 30 575
5/32 in (4.0 mm) DC+ 1.4 (55) 27 440
5/32 in (4.0 mm) DC+ 2.2 (85) 30 575
5/32 in (4.0 mm) DC+ 2.9 (115) 32 700