Diameters / Packaging
|
Diameters |
10lb Spool |
25lb Steel Spool |
50lb Coil |
500lb Speed-Feed® Drum |
|---|---|---|---|---|
| 0.045 | ED037262 | ED031131 | ||
| 1/16 | ED037263 | ED031132 | ||
| 5/64 | ED031133 | ED019887 | ED037493 | |
| 7/64 | ED019888 |
DETAILS
Iron-based wire with a large amount of chromium carbides in a hard matrix. Designed to exhibit stress-relieve cross-check cracking. They can be used on carbon, low alloy, manganese, stainless and cast iron parts. Deposit thicknesses are generally limited to 2 layers. Use in applications with severe abrasion accompanied by low or moderate impact, works best in Metal-to-Earth applications.
Features
- Can be used on carbon, low alloy, manganese steel, stainless steel, and cast iron
- Deposit is limited to two layers
- Deposits feature higher alloy levels than to resist both abrasion and moderate impact
- Can be used at temperatures up to 704°C (1300°F)
Disclaimers
Service Information
You May Also Need
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
MECHANICAL PROPERTIES
| Classification | Number of layer | Hardness Rockwell C | Mass Loss (G65) |
|---|---|---|---|
| Typical Result | 1 Layer | 50-55 | 0.67 |
| Typical Result | 2 Layers | 55-58 | 0.20 |
DEPOSIT COMPOSITION
| Classification | Number of layer | %Al | %C | %Cr | %Mn | %Si |
|---|---|---|---|---|---|---|
| Typical Result | 2 Layers | 0.3-0.4 | 4.0-4.6 | 18.5-22.9 | 1.0-1.8 | 0.5-0.9 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity |
ESO
mm (in.) |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
Deposition Rate
kg/hr (lb/hr) |
|---|---|---|---|---|---|---|
| .045" (1.1 mm) | DC+ | 19 (1) | 5.1 (200) | 21 | 125 | 1.9 (4.1) |
| .045" (1.1 mm) | DC+ | 19 (1) | 10.2 (400) | 25 | 185 | 3.7 (8.2) |
| .045" (1.1 mm) | DC+ | 19 (1) | 12.7 (500) | 27 | 210 | 4.7 (10.3) |
| 1/16" (1.6 mm) | DC+ | 22 (1) | 5.1 (200) | 28 | 240 | 3.4 (7.6) |
| 1/16" (1.6 mm) | DC+ | 22 (1) | 7.6 (300) | 31 | 300 | 5.1 (11.2) |
| 1/16" (1.6 mm) | DC+ | 22 (1) | 11.4 (450) | 33 | 350 | 7.5 (16.6) |
| 5/64" (2.0 mm) | DC+ | 32 (1) | 3.2 (125) | 26 | 250 | 3.4 (7.4) |
| 5/64" (2.0 mm) | DC+ | 32 (1) | 5.1 (200) | 30 | 350 | 5.4 (12.0) |
| 5/64" (2.0 mm) | DC+ | 32 (1) | 6.4 (250) | 32 | 400 | 6.8 (15.1) |
| 7/64" (2.8 mm) | DC+ | 29 (1) | 1.9 (75) | 27 | 250 | 3.4 (7.4) |
| 7/64" (2.8 mm) | DC+ | 29 (1) | 3.2 (125) | 30 | 340 | 5.4 (11.9) |
| 7/64" (2.8 mm) | DC+ | 29 (1) | 4.4 (175) | 32 | 420 | 7.5 (16.5) |
NOTES
| Note |
|---|
| Deposit thickness limit is two layers unless high travel speed is used to obtain very closely spaced check cracks. Many layers can be used with high travel speed and small bead sizes to ensure close-spaced check cracks. |
| Lincore® 60-O deposit cross cracks (commonly called cross-checking) on cooling. This is desirable, since cross-cracking of the deposit relieves cooling stresses and prevents spalling. |