Lincore® BU

Flux-Cored Self-Shielded (FCAW-S)

Ideal for building up on carbon and low alloy steels. Use as an underbase for carbon steel parts prior to hardfacing.

Diameter

Select Diameter

  • 5/64 in (2.0 mm)
  • 7/64 in (2.8 mm)

Package

Select Package

  • 25 lb Spool
  • 50 lb Coil
Buy Now

DETAILS

Ideal for building up on carbon and low alloy steels. Use as an underbase for carbon steel parts prior to hardfacing. Great compressive strength under heavy loading. Deposits are generally crack free, machinable and can be flame cut. Deposit thickness is unlimited.

Features

  • Unlimited layers. Can also be used as the final hardfacing layer for non-severe metal-to-metal wear applications
  • Provides a tough machinable deposit for build-up or final overlay
  • Delivers non-severe metal-to-metal wear with outstanding crack resistance
  • Ideal for rebuilding worn parts to near final dimensions before applying final hardfacing layers which are more wear resistant

Typical Applications

  • Crane, Kiln
  • Rolls,Tractor
  • Mine Car, Shovel

Welding Positions

  • Flat/Horizontal

Disclaimers

Warning -

Cancer and Reproductive Harm -

www.P65Warnings.ca.gov

Service Information

You May Also Need

50lb Coil Ultracore 70C

Lincore® BU Flux-Cored (FCAW-S) Wire

ED022065
33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Lincore® BU-G Flux-Cored (FCAW-G) Wire

ED029079
33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Lincore® BU-G Flux-Cored (FCAW-G) Wire

ED029080
33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Lincore® BU Flux-Cored (FCAW-S) Wire

ED031115
View All

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

MECHANICAL PROPERTIES

Classification Hardness Rockwell B
Typical Result 78-90
Typical Result, Work-hardened 86-98

DEPOSIT COMPOSITION

Classification %Al %C %Mn %Si
Typical Result 1.50 0.24 0.50 0.25

TYPICAL OPERATING PROCEDURES

Diameter Polarity ESO
mm (in.) 		Wire Feed Speed
m/min (in/min) 		Voltage
volts 		Approx. Current
amps 		Deposition Rate
kg/hr (lb/hr)
5/64 in (2.0 mm) DC+ 50 (2) 5.1 (200) 29 280 4.6 (10.1)
5/64 in (2.0 mm) DC+ 50 (2) 6.1 (240) 30 315 5.5 (12.1)
5/64 in (2.0 mm) DC+ 50 (2) 6.6 (260) 30 330 6.1 (13.2)
5/64 in (2.0 mm) DC+ 50 (2) 7.6 (300) 31 350 6.9 (15.2)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 3.4 (135) 26 360 5.7 (12.6)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 3.8 (150) 27 385 6.3 (13.9)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 4.4 (175) 28 420 7.3 (16.0)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.1 (200) 29 450 8.2 (18.1)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.9 (235) 30 470 9.6 (21.1)