Lincore® M Flux-Cored (FCAW-S) Wire

Flux-Cored Self-Shielded (FCAW-S) | ED011162

CLASSIFICATIONS:
EN/ISO : T Fe9

Lincore® M Flux-Cored Wire is an austenitic manganese deposit that work-hardens, deposit resists severe impact as well as moderate abrasion on typical applications including Hammers, Dredge parts, Crushers, Breaker bars and Buckets (Severe Impact)

Diameter

Select Diameter

  • 0.045 in (1.1 mm)
  • 1/16 in (1.6 mm)
  • 5/64 in (2.0 mm)
  • 7/64 in (2.8 mm)

Package

Select Package

  • 50 lb (22.7 kg) Coil
  • 125 lb (56.7 kg) Speed-Feed® Drum
  • 600 lb (272 kg) Speed-Feed® Drum
Buy Now

DETAILS

Lincore® M Flux-Cored Wire is recommended for build-up and repair of Hadfield-type austenitic manganese materials as well as carbon and low alloy steels. Unlimited layers with proper preheat and interpass temperatures and procedures As with all austenitic manganese welding products, interpass temperatures should be limited to 260°C (500°F) maximum. A stringer bead, or at most, a slight weave is recommended to limit heat build-up. Excessive heat build-up causes manganese carbide precipitation which damages the toughness of austenitic manganese. Composition and properties depend upon dilution. Single layer deposit properties depend upon base metal and/or build-up material.

Features

  • Deposit resists severe impact as well as moderate abrasion
  • Produces an austenitic manganese deposit that work-hardens
  • Recommended for build-up and repair of Hadfield-type austenitic manganese materials as well as carbon and low alloy steels
  • Unlimited layers with proper preheat and interpass temperatures and procedures

Disclaimers

Warning -

Cancer and Reproductive Harm -

www.P65Warnings.ca.gov

Service Information

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

MECHANICAL PROPERTIES

Classification Hardness Rockwell C
Typical Result 18-28
Typical Result, Work-hardened 30-48

DEPOSIT COMPOSITION

Classification %C %Cr %Mn %Ni %Si
Typical Result 0.6 4.9 13.0 0.5 0.4

TYPICAL OPERATING PROCEDURES

Diameter Polarity ESO
mm (in.) 		Wire Feed Speed
m/min (in/min) 		Voltage
volts 		Approx. Current
amps 		Deposition Rate
kg/hr (lb/hr)
0.045 in (1.1 mm) DC+ 25 (1) 5.1 (200) 22 80 1.5 (3.3)
0.045 in (1.1 mm) DC+ 25 (1) 8.9 (350) 24 145 2.7 (6.0)
0.045 in (1.1 mm) DC+ 25 (1) 12.7 (500) 26 185 4.4 (9.6)
1/16 in (1.6 mm) DC+ 30 (1 1/8) 3.8 (150) 23 130 2.2 (4.9)
1/16 in (1.6 mm) DC+ 30 (1 1/8) 6.4 (250) 25 200 3.9 (8.6)
1/16 in (1.6 mm) DC+ 30 (1 1/8) 8.9 (350) 27 250 5.6 (12.4)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 3.2 (125) 24 240 2.9 (6.4)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 4.4 (175) 27 300 4.2 (9.3)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 6.4 (250) 29 360 6.2 (13.6)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 1.9 (75) 25 240 3.5 (7.8)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.2 (125) 27 360 6.2 (13.6)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.8 (150) 28 395 7.5 (16.6)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 1.9 (75) 25 240 3.6 (8.0)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 4.4 (175) 30 400 8.8 (19.5)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.7 (225) 32 455 11.6 (25.6)

NOTES

Note
As with all austenitic manganese welding products, interpass temperatures should be limited to 260°C (500°F) maximum.
A stringer bead, or at most, a slight weave is recommended to limit heat build-up. Excessive heat build-up causes manganese carbide precipitation that damages the toughness of austenitic manganese.