Diameters / Packaging
Diameters |
50 lb Carton |
---|---|
1/4 x 18 in (6.4 x 450 mm) | EDM13181218 |
1/8 x 14 in (3.2 x 350 mm) | EDM13181214 |
3/16 x 18 in (4.8 x 450 mm) | EDM13181216 |
5/32 x 14 in (4.0 x 350 mm) | EDM13181215 |
7/32 x 18 in (5.6 x 450 mm) | EDM13181217 |
DETAILS
Features
- High deposition rates
- Smooth bead appearance
- Minimal spatter
- Shallow penetration
Typical Applications
- Large welds
- Slightly downhill (15° max) positions
- Multiple pass welding
Welding Positions
- Flat/Horizontal
Shielding Gas
- Not Applicable
Disclaimers
Service Information
Documentation
You May Also Need
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
CONFORMANCE
CONFORMANCES | SPECIFICATION | CLASSIFICATION |
---|---|---|
AWS | AWS A5.1 | E7024 |
MECHANICAL PROPERTIES
Classification |
Yield Strength @ 0.2% Offset
MPa (ksi) |
Tensile Strength
MPa (ksi) |
Elongation
% |
Hardness Rockwell B |
---|---|---|---|---|
E7024 Requirement | 400 (58) min. | 480 (70) min. | 17 min. | |
Typical Result, As-welded | 450-530 (65-76) | 520-610 (76-88) | 22-30 | 82-93 |
DEPOSIT COMPOSITION
Classification | %C | %Cr | %Mn | %Mo | %Ni | %P | %S | %Si | %V | %Mn+Ni+Cr+Mo+V |
---|---|---|---|---|---|---|---|---|---|---|
E7024 Requirement | 0.15 max. | 0.20 max. | 1.25 max. | 0.30 max. | 0.30 max. | 0.035 max. | 0.035 max. | 0.90 max. | 0.08 max. | 1.50 max. |
Typical Result | 0.05-0.11 | 0.03-0.06 | 0.67-1.13 | 0.02 max. | 0.01-0.05 | 0.012-0.021 | 0.004-0.011 | 0.25-0.54 | 0.02-0.03 | 0.79-1.25 |
TYPICAL OPERATING PROCEDURES
Diameter | Polarity |
Current
Amps |
---|---|---|
1/8 in (3.2 mm) | AC | 115-175 |
1/8 in (3.2 mm) | DC± | 100-160 |
5/32 in (4.0 mm) | AC | 180-240 |
5/32 in (4.0 mm) | DC± | 160-215 |
3/16 in (4.8 mm) | AC | 240-300 |
3/16 in (4.8 mm) | DC± | 220-280 |
7/32 in (5.6 mm) | AC | 300-380 |
7/32 in (5.6 mm) | DC± | 270-340 |
1/4 in (6.4 mm) | AC | 340-440 |
1/4 in (6.4 mm) | DC± | 320-400 |