Non heat treatable Low Magnesium Manganese alloy used for 5454 base material especially in elevated temperature applications above 150 deg F / 65 deg C .
Traits
- Matching filler alloy for welding 5454 base alloys
- Low magnesium content to closely match the base material chemistry
- Moderate strength applications
Positions de soudage
- All except vertical down
Gaz de protection
- 100% Argon Argon / Helium Mixtures Flow Rate: 30 - 50 CFH
Disclaimers
Des informations de service
Vous pourriez également avoir besoin
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
CONFORMANCE
CONFORMANCES | SPECIFICATION | CLASSIFICATION |
---|---|---|
AWS | AWS A5.10 | ER5554 |
WIRE COMPOSITION
Classification | %Be | %Mg | %Zn | %Cr | %Cu | %Fe | %Mn | %Si | %Ti |
---|---|---|---|---|---|---|---|---|---|
ER5554 Requirement | 0.0003 max. | 2.4 - 3.0 | 0.25 max. | 0.05 - 0.20 | 0.10 max. | 0.40 max. | 0.50 - 1.0 | 0.25 max. | 0.05 - 0.20 |
Typical Result | 0.0002 max. | 2.6 | 0.00 | 0.08 | 0.01 | 0.13 | 0.7 | 0.06 | 0.09 |
TYPICAL OPERATING PROCEDURES
Diameter | Shielding Gas |
Gas Flow
L/min (CFH) |
Polarity |
CTWD
mm (in.) |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
---|---|---|---|---|---|---|---|
0.9 mm (.035") | 100% Ar | 14-24 (30-50) | DC+ | 12.7 (¹/₂) - 15.9 (⁵/₈) | 19.6 (770) | 21.6 | 185 |
1.2 mm (3/64") | 100% Ar | 14-24 (30-50) | DC+ | 12.7 (¹/₂) - 15.9 (⁵/₈) | 12.7 (500) | 23.0 | 210 |
1.6 mm (1/16") | 100% Ar | 14-24 (30-50) | DC+ | 12.7 (¹/₂) - 15.9 (⁵/₈) | 9.1 (360) | 24.8 | 280 |
2.4 mm (3/32") | 100% Ar | 85 (180) | DC+ | 19.0 (³/₄) | 8.0 (315) | 28.0 | 500 |
3.2 mm (1/8") | 100% Ar | 85 (180) | DC+ | 19.0 (³/₄) | 5.1 (200) | 30.3 | 535 |