Ideal for building up on carbon and low alloy steels. Use as an underbase for carbon steel parts prior to hardfacing. Great compressive strength under heavy loading. Deposits are generally crack free, machinable and can be flame cut. Deposit thickness is unlimited.Use as an underbase for carbon steel parts prior to hardfacing build-up appliacation.
Caractéristiques
- Use on low alloy steels
- Deposit is unlimited layers
- Delivers deposits with moderate hardness for build-up or as final overlay
- Provides some resistance to metal-to-metal wear and moderate impact
- Delivers deposits with moderate hardness for build-up or as final overlay
Service d'information
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. Page de recherche SDS
Consultez le résultat de test Clause de non-responsabilité
MECHANICAL PROPERTIES
Classification | Hardness Rockwell C |
---|---|
Typical Result | 21-33 |
Typical Result, Work-hardened | 40-42 |
DEPOSIT COMPOSITION
Classification | Number of layer | %C | %Cr | %Mn | %Mo | %Si |
---|---|---|---|---|---|---|
Typical Result | 4 Layers | 0.08 | 0.9 | 1.6 | 0.3 | 0.5 |
TYPICAL OPERATING PROCEDURES
Diameter | Shielding Gas | Polarity |
ESO
mm (in.) |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
Deposition Rate
kg/hr (lb/hr) |
---|---|---|---|---|---|---|---|
0.045 in (1.1 mm) | 75% Ar / 25% CO2 | DC+ | 16 (5/8) | 5.1 (200) | 29 | 175 | 1.7 (3.7) |
0.045 in (1.1 mm) | 75% Ar / 25% CO2 | DC+ | 16 (5/8) | 7.6 (300) | 30 | 240 | 2.6 (5.8) |
0.045 in (1.1 mm) | 75% Ar / 25% CO2 | DC+ | 16 (5/8) | 10.2 (400) | 32 | 300 | 3.6 (7.9) |
0.045 in (1.1 mm) | 90% Ar / 10% CO2 | DC+ | 20 (3/4) | 5.1 (200) | 25 | 215 | 2.1 (4.7) |
0.045 in (1.1 mm) | 90% Ar / 10% CO2 | DC+ | 20 (3/4) | 7.6 (300) | 27 | 250 | 3.1 (6.9) |
0.045 in (1.1 mm) | 90% Ar / 10% CO2 | DC+ | 20 (3/4) | 10.2 (400) | 29 | 285 | 4.1 (9.1) |
0.045 in (1.1 mm) | 98% Ar / 2% O2 | DC+ | 20 (3/4) | 5.1 (200) | 25 | 210 | 2.0 (4.5) |
0.045 in (1.1 mm) | 98% Ar / 2% O2 | DC+ | 20 (3/4) | 7.6 (300) | 26 | 280 | 3.2 (7.1) |
0.045 in (1.1 mm) | 98% Ar / 2% O2 | DC+ | 20 (3/4) | 10.2 (400) | 28 | 315 | 4.4 (9.7) |
1/16 in (1.6 mm) | 75% Ar / 25% CO2 | DC+ | 20 (3/4) | 3.8 (150) | 27 | 280 | 2.8 (6.1) |
1/16 in (1.6 mm) | 75% Ar / 25% CO2 | DC+ | 20 (3/4) | 6.4 (250) | 29 | 370 | 4.8 (10.5) |
1/16 in (1.6 mm) | 75% Ar / 25% CO2 | DC+ | 20 (3/4) | 8.9 (350) | 31 | 460 | 6.8 (14.9) |
1/16 in (1.6 mm) | 90% Ar / 10% CO2 | DC+ | 20 (3/4) | 3.8 (150) | 25 | 270 | 2.6 (5.7) |
1/16 in (1.6 mm) | 90% Ar / 10% CO2 | DC+ | 20 (3/4) | 6.4 (250) | 27 | 375 | 4.9 (10.8) |
1/16 in (1.6 mm) | 90% Ar / 10% CO2 | DC+ | 20 (3/4) | 8.9 (350) | 29 | 470 | 7.2 (15.9) |
1/16 in (1.6 mm) | 98% Ar / 2% O2 | DC+ | 20 (3/4) | 3.8 (150) | 24 | 290 | 2.8 (6.1) |
1/16 in (1.6 mm) | 98% Ar / 2% O2 | DC+ | 20 (3/4) | 6.4 (250) | 26 | 390 | 5.0 (11.1) |
1/16 in (1.6 mm) | 98% Ar / 2% O2 | DC+ | 20 (3/4) | 8.9 (350) | 28 | 490 | 7.3 (16.1) |