Innershield® NR®-152 Flux-Cored (FCAW-S) Wire

Flux-Cored Self-Shielded (FCAW-S) | ED012186

CLASSIFICATIONS:
E71T-14
E71T14S

Innershield® NR®-152 from Lincoln Electric is designed for high speed welding of specialty coated steels.

Diameter

Select Diameter

  • 0.045 in (1.1 mm)
  • 0.068 in (1.7 mm)

Package

Select Package

  • 22.7 KG COIL

DETAILS

Designed for high speed welding of specialty coated steels. Recommended for single pass welding on material thicknesses from 0.8 to 4.8 mm (0.030 to 3/16 in).

Features

  • Designed for high speed welding of specially coated steels
  • Soft, consistent arc
  • Porosity resistant
  • Excellent overlapping capabilities
  • Ideal for robotic applications
  • Warning: NR-5 is NOT recommended for welding multiple passes.
  • Notes: The preferred drag angle is 15°, however, NR-152 is capable of welding at zero drag angle, facilitating easy fixturing in automatic applications.

Service Information

You May Also Need

K126 Classic 350A FCAW-SS

K126® Classic® Innershield® 350A FCAW-SS Welding Gun 15 ft 062-332

K126-2
Gun Receiver Bushing

Gun Receiver Bushing for Lincoln Electric® Guns

K1500-1
Drive Roll and Guide Tube Kit

Drive roll kit (2R) 1.8 mm

KP1697-068
Image not found

Nozzle Insulated (Nose Cone)

KP1987-1
View All

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

CONFORMANCE

CONFORMANCES SPECIFICATION CLASSIFICATION
AWS AWS A5.20 E71T-14
AWS AWS A5.36 E71T14S

MECHANICAL PROPERTIES

Classification Polarity Transverse Tensile Strength
MPa (ksi) 		Longitudinal Face Bend
E71T-14 Requirement DC- 480 (70) min. No opening in excess of 1/8 inch
E71T14S Requirement DC- 480 (70) min. No opening in excess of 1/8 inch
Typical Result, As-welded DC- 530-570 (76-83) Passed

DEPOSIT COMPOSITION

Classification %Al %C %Mn %P %S %Si
Typical Result 2.0-3.9 0.34 1.13 0.016 0.003 0.27

TYPICAL OPERATING PROCEDURES

Diameter Polarity CTWD
mm (in.) 		Wire Feed Speed
m/min (in/min) 		Voltage
volts 		Approx. Current
amps 		Melt-off Rate
kg/hr (lb/hr) 		Deposition Rate
kg/hr (lb/hr) 		Efficiency
%
1/16 in (1.6 mm) DC- 16 (5/8) 0.8 (30) 13-14 90 0.5 (1.3) 0.5 (1.2) 92
1/16 in (1.6 mm) DC- 16 (5/8) 1.0 (40) 14-15 115 0.8 (1.8) 0.7 (1.6) 88
1/16 in (1.6 mm) DC- 16 (5/8) 1.3 (50) 15-16 140 0.9 (2.2) 0.9 (2.0) 90
1/16 in (1.6 mm) DC- 16 (5/8) 1.8 (70) 16-17 185 1.4 (3.1) 1.3 (2.8) 90
1/16 in (1.6 mm) DC- 16 (5/8) 2.8 (110) 19-20 265 2.1 (4.8) 2.0 (4.4) 91
0.068 in (1.7 mm) DC- 19 (3/4) 0.8 (30) 13-14 68 0.7 (1.6) 0.6 (1.4) 87
0.068 in (1.7 mm) DC- 19 (3/4) 1.0 (40) 13-14 95 0.9 (2.2) 0.9 (1.9) 86
0.068 in (1.7 mm) DC- 19 (3/4) 1.3 (50) 14-15 120 1.2 (2.7) 1.1 (2.4) 88
0.068 in (1.7 mm) DC- 19 (3/4) 1.5 (60) 15-16 145 1.4 (3.3) 1.3 (2.9) 87
0.068 in (1.7 mm) DC- 19 (3/4) 2.0 (80) 16-17 190 1.9 (4.4) 1.8 (3.9) 88
0.068 in (1.7 mm) DC- 19 (3/4) 2.8 (110) 20-21 240 2.7 (6.0) 2.4 (5.4) 90