Submerged Arc Family

Diametre / Ambalaj

Diametre

Lincolnweld® 860®

Submerged Arc Welding (SAW)

800 Series Neutral Flux

Acest produs nu se mai fabrică sau nu mai este disponibil pentru vânzare.

DETALII

Caracteristici

  • Industry standard for submerged arc welding applications
  • Excellent operating characteristics in a variety of general welding applications
  • Capable of producing weld deposits with impact toughness exceeding 27 J (20 ft•lbf) at -40°C (-40°F) with Lincolnweld® L-61
  • Actual (Type 3.1) certificates for each lot of flux showing chemical composition, particle size and moisture level are available in the certificate center of lincolnelectric.com
  • Mild Steel Lincolnweld® L-50®, L-56®, L-60, L-61®, LA-71, L-S3 Low Alloy Steel Lincolnweld® L-70, LA-75, LA-82, LA-85

Aplicații tipice

  • AASHTO Fracture Critical applications with Lincolnweld® L-61® wire
  • Pipe and other double ending applications
  • General purpose structural and multiple pass welds
  • Storage tanks using L-61® or LA-85

Caracteristici speciale

  • Basicity Index: 1.1 Density: 1.4 g/cm3

Disclaimers

Warning -

Cancer and Reproductive Harm -

www.P65Warnings.ca.gov

Informații despre service

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. Pagina de căutare FDS

Consultare rezultat test declinare a responsabilității

MECHANICAL PROPERTIES

Wire Classification Postweld Heat Treatment Yield Strength @ 0.2% Offset
MPa (ksi)
Tensile Strength
MPa (ksi)
Elongation
%
Charpy V-Notch
J (ft-lbs) @ -30°C (-20°F)
Charpy V-Notch
J (ft-lbs) @ -40°C (-40°F)
Charpy V-Notch
J (ft-lbs) @ -45°C (-50°F)
Charpy V-Notch
J (ft-lbs) @ -50°C (-60°F)
Lincolnweld® L-50® F7A2-EM13K-H4 As-welded 420 (61) 540 (78) 30 88 (65)
Lincolnweld® L-56® F7A2-EH11K-H4 As-welded 500 (72) 610 (88) 28 75 (55)
Lincolnweld® L-56® F7P2-EH11K-H4 1 hour @ 620°C (1150°F) 430 (62) 560 (81) 31 96 (71)
Lincolnweld® L-60 F6A2-EL12-H4 As-welded 370 (54) 440 (64) 33 198 (146)
Lincolnweld® L-61® F6P5-EM12K-H8 1 hour @ 620°C (1150°F) 370 (53) 480 (69) 35 148 (109)
Lincolnweld® L-61® F7A4-EM12K-H8 As-welded 420 (61) 510 (74) 30 145 (107)
Lincolnweld® L-70 F7A2-EA1-A2-H4 As-welded 470 (68) 560 (81) 28 96 (71)
Lincolnweld® L-70 F7P2-EA1-A2-H4 1 hour @ 620°C (1150°F) 440 (64) 540 (78) 29 94 (69)
Lincolnweld® LA-71 F7A2-EM14K-H4 As-welded 460 (67) 560 (81) 30 145 (107)
Lincolnweld® LA-71 F7P2-EM14K-H4 1 hour @ 620°C (1150°F) 420 (61) 540 (78) 30 123 (91)
Lincolnweld® LA-75 F7A2-ENi1K-Ni1-H4 As-welded 470 (68) 570 (82) 29 115 (85)
Lincolnweld® LA-75 F7P2-ENi1K-Ni1-H4 1 hour @ 620°C (1150°F) 410 (60) 530 (77) 31 123 (91)
Lincolnweld® LA-81 (LNS 140TB) F9TA6G-EA2TiB As-welded 610 (88) 670 (97) 27 33 (24)
Lincolnweld® LA-85 (LNS 165) F8A4-ENi5-Ni5-H4 As-welded 490 (71) 580 (84) 27 119 (88)
Lincolnweld® L-S3 (LNS133U,L50M) F7A2-EH12K-H4 As-welded 420 (61) 520 (75) 30 138 (102)
Pipeliner® LA-85 F8A4-ENi5-Ni5-H4 As-welded 490 (71) 580 (84) 27 119 (88)

DEPOSIT COMPOSITION

Wire Classification %B %C %Cr %Cu %Mn %Mo %Ni %P %S %Si %Ti %Ti+V+Zr Diffusible Hydrogen
mL/100g Weld Metal
Lincolnweld® L-50® F7A2-EM13K-H4 0.04 0.09 1.74 0.014 0.009 0.54 3
Lincolnweld® L-56® F7A2-EH11K-H4 0.05 0.09 2.12 0.018 0.004 0.86 2
Lincolnweld® L-56® F7P2-EH11K-H4 0.05 0.09 2.12 0.018 0.040 0.86 2
Lincolnweld® L-60 F6A2-EL12-H4 0.04 0.07 1.04 0.016 0.010 0.25 4
Lincolnweld® L-61® F6P5-EM12K-H8 0.05 0.06 1.52 0.018 0.010 0.36 2
Lincolnweld® L-61® F7A4-EM12K-H8 0.05 0.06 1.52 0.018 0.009 0.35 2
Lincolnweld® L-70 F7A2-EA1-A2-H4 0.04 0.08 1.31 0.52 0.015 0.009 0.28 3
Lincolnweld® L-70 F7P2-EA1-A2-H4 0.05 0.08 1.28 0.53 0.015 0.009 0.26 3
Lincolnweld® LA-71 F7A2-EM14K-H4 0.05 0.13 1.76 0.016 0.008 0.57 0.020 3
Lincolnweld® LA-71 F7P2-EM14K-H4 0.05 0.13 1.74 0.016 0.009 0.06 0.020 3
Lincolnweld® LA-75 F7A2-ENi1K-Ni1-H4 0.05 0.03 0.10 1.64 0.01 0.86 0.014 0.009 0.63 0.01 2
Lincolnweld® LA-75 F7P2-ENi1K-Ni1-H4 0.05 0.03 0.10 1.68 0.00 0.86 0.014 0.010 0.61 0.01 2
Lincolnweld® LA-81 (LNS 140TB) F9TA6G-EA2TiB 0.0037 0.06 0.15 1.35 0.21 0.011 0.004 0.31 0.032
Lincolnweld® LA-85 (LNS 165) F8A4-ENi5-Ni5-H4 0.04 0.08 1.58 0.22 0.87 0.020 0.003 0.30 3
Lincolnweld® L-S3 (LNS133U,L50M) F7A2-EH12K-H4 0.05 0.10 1.77 0.015 0.009 0.45 3
Pipeliner® LA-85 F8A4-ENi5-Ni5-H4 0.04 0.08 1.58 0.22 0.87 0.020 0.003 0.30 3

FLUX COMPOSITION

Classification %Al2O3 %CaF2 %CaO %MgO %MnO %Na2O %SiO2 %TiO2 %ZrO2 %Metal Alloys
Typical Result 30 13 2 18 11 2 19 2 0 3