Diameters / Packaging
|
Diameters |
|---|
DETAILS
Ideal for building up on carbon and low alloy steels. Use as an underbase for carbon steel parts prior to hardfacing. Great compressive strength under heavy loading. Deposits are generally crack free, machinable and can be flame cut. Deposit thickness is unlimited.
Features
- For automatic and semiautomatic operation on mild and low alloy steels
- Unlimited deposit thickness
- Intended for build-up before final overlay, and as a final surface for metal-to-metal wear with moderate impact
Typical Applications
- Tractor rollers, Trunnions,
- Idler, Crane Wheels
- Shafts, Track Rails
Welding Positions
- Flat/Horizontal
Service Information
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
MECHANICAL PROPERTIES
| Flux | Classification | Number of layer | Hardness Rockwell C |
|---|---|---|---|
| Lincolnweld® 801® | Typical Result | 6 | 27 |
DEPOSIT COMPOSITION
| Flux | Classification | %C | %Mn | %Mo | %Si |
|---|---|---|---|---|---|
| Lincolnweld® 801® | Typical Result | 0.11 | 2.5 | 0.5 | 0.4 |
| Lincolnweld® 801® | Typical Result | 0.11 | 2.5 | 0.5 | 0.4 |
| Lincolnweld® 801® | Typical Result | 0.11 | 2.7 | 0.5 | 0.6 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
|---|---|---|---|---|
| 3/32 in (2.4 mm) | DC+ | 1.5 (60) | 26 | 220 |
| 3/32 in (2.4 mm) | DC+ | 3.0 (120) | 27 | 360 |
| 3/32 in (2.4 mm) | DC+ | 4.6 (180) | 28 | 500 |
| 1/8 in (3.2 mm) | DC+ | 1.3 (50) | 27 | 310 |
| 1/8 in (3.2 mm) | DC+ | 2.0 (80) | 28 | 450 |
| 1/8 in (3.2 mm) | DC+ | 2.8 (110) | 28 | 600 |