Diameters / Packaging
|
Diameters |
|---|
DETAILS
Ideal for building up on carbon and low alloy steels. Use as an underbase for carbon steel parts prior to hardfacing. Great compressive strength under heavy loading. Deposits are generally crack free, machinable and can be flame cut. Deposit thickness is unlimited.
Features
- Deposit thickness is unlimited.
- Intended for rolling and sliding metal-to-metal wear with moderate impact and abrasion.
- Recommended as final overlay where medium hardness and good machinability are required.
- For automatic and semiautomatic operation on mild and low alloy steels.
- Weld with Lincore® 801 or Lincore® 802
Typical Applications
- Tractor rollers, Track Rails, Idlers
- Trunnions, Crane Wheels
- Caster Rolls, Mine Car Wheels
- Shafts, Bearing Journals
Welding Positions
- Flat/Horizontal
Service Information
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
MECHANICAL PROPERTIES
| Flux | Classification | Hardness Rockwell C |
|---|---|---|
| Lincolnweld® 801® | Typical Result | 39 |
DEPOSIT COMPOSITION
| Flux | Classification | %C | %Cr | %Mn | %Mo | %Si |
|---|---|---|---|---|---|---|
| Lincolnweld® 801® | Typical Result | 0.19 | 2.3 | 1.7 | 0.5 | 0.6 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
|---|---|---|---|---|
| 1/8 in (3.2 mm) | DC+ | 1.3 (50) | 28 | 340 |
| 1/8 in (3.2 mm) | DC+ | 2.5 (100) | 28 | 500 |
| 1/8 in (3.2 mm) | DC+ | 3.8 (150) | 28 | 660 |