Diameters / Packaging
|
Diameters |
|---|
DETAILS
Ideal for building up on carbon and low alloy steels. Use as an underbase for carbon steel parts prior to hardfacing. Great compressive strength under heavy loading. Deposits are generally crack free, machinable and can be flame cut. Deposit thickness is unlimited. Used in Metal-to-Metal wear applications, works best in impact applications.
Features
- Use on low alloy steels
- Deposit is unlimited layers
- Higher wear continuous caster rolls
- Works well with Lincolnweld® 801®, Lincolnweld® 802®
Typical Applications
- Castor Rolls, Coal Mining cutting teeth, Crusher rolls, Crane Wheels
- Drill Stems, Drive sprockets , Dredge cutter teeth, Idler, Journals
- Mine car wheel, Muller plows & tires, Ore chute baffles, Shafts
- Track Rails, Tractor rollers, Tractor Pads, Trunnions
Welding Positions
- Flat, Horizontal
Service Information
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
MECHANICAL PROPERTIES
| Flux | Classification | Hardness Rockwell C |
|---|---|---|
| Lincolnweld® 802® | Typical Result | 42 |
DEPOSIT COMPOSITION
| Flux | Classification | %C | %Cr | %Mn | %Mo | %N | %Ni | %Si | %V | %W |
|---|---|---|---|---|---|---|---|---|---|---|
| Lincolnweld® 802® | Typical Result | 0.06 | 11.7 | 1.9 | 1.4 | 0.08 | 3.7 | 0.6 | 0.29 | 0.27 |
TYPICAL OPERATING PROCEDURES
| Flux | Diameter | Polarity |
CTWD
mm (in.) |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
|---|---|---|---|---|---|---|
| Lincolnweld® 802® | 1/8" (3.2 mm) | DC+ | 38 (1¹/₂) | 2.7 (105) | 28 | 400-600 |