DETAILS
Ideal for building up on carbon and low alloy steels. Use as an underbase for carbon steel parts prior to hardfacing. Great compressive strength under heavy loading. Deposits are generally crack free, machinable and can be flame cut. Deposit thickness is unlimited. Used in Metal-to-Metal wear applications, works best in impact applications.
Features
- To be used on carbon steel and low alloy steel
- Unlimited layers with proper preheat and interpass temperatures and procedures
- Produces a deposit which resists metal-to-metal wear and mild abrasion
- The deposit results in an even harder material when used with the Bulk Tungsten Carbide process
Service Information
Documentation
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
MECHANICAL PROPERTIES
Classification | Shielding Gas | Hardness Rockwell C |
---|---|---|
Typical Result | 98% Ar, 2% O2 | 56-59 |
Typical Result | 75% Ar, 25% CO2 | 59-61 |
DEPOSIT COMPOSITION
Classification | Product Size | Number of layer | Shielding Gas | %C | %Cr | %Mn | %Mo | %Si |
---|---|---|---|---|---|---|---|---|
Typical Result | .045" (1.1 mm) | 2 Layers | 75% Ar, 25% CO2 | 0.39 | 5.6 | 1.2 | 0.6 | 0.8 |
Typical Result | .045" (1.1 mm) | 2 Layers | 98% Ar, 2% O2 | 0.47 | 6.4 | 1.4 | 0.6 | 1.0 |
Typical Result | 1/16" (1.6 mm) | 2 Layers | 75% Ar, 25% CO2 | 0.41 | 5.3 | 1.2 | 0.6 | 0.8 |
Typical Result | 1/16" (1.6 mm) | 2 Layers | 98% Ar, 2% O2 | 0.45 | 5.5 | 1.2 | 0.6 | 1.0 |
TYPICAL OPERATING PROCEDURES
Diameter | Shielding Gas | Polarity |
ESO
mm (in.) |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
Deposition Rate
kg/hr (lb/hr) |
---|---|---|---|---|---|---|---|
0.045 in (1.1 mm) | 75% Ar / 25% CO2 | DC+ | 16 (5/8) | 5.1 (200) | 27 | 165 | 2.0 (4.3) |
0.045 in (1.1 mm) | 75% Ar / 25% CO2 | DC+ | 16 (5/8) | 7.6 (300) | 29 | 225 | 3.0 (6.7) |
0.045 in (1.1 mm) | 75% Ar / 25% CO2 | DC+ | 16 (5/8) | 10.2 (400) | 31 | 290 | 4.2 (9.2) |
0.045 in (1.1 mm) | 90% Ar / 10% CO2 | DC+ | 20 (3/4) | 5.1 (200) | 25 | 145 | 2.1 (4.7) |
0.045 in (1.1 mm) | 90% Ar / 10% CO2 | DC+ | 20 (3/4) | 7.6 (300) | 28 | 195 | 3.3 (7.2) |
0.045 in (1.1 mm) | 90% Ar / 10% CO2 | DC+ | 20 (3/4) | 10.2 (400) | 30 | 245 | 4.4 (9.7) |
0.045 in (1.1 mm) | 98% Ar / 2% O2 | DC+ | 20 (3/4) | 5.1 (200) | 25 | 145 | 2.3 (5.1) |
0.045 in (1.1 mm) | 98% Ar / 2% O2 | DC+ | 20 (3/4) | 7.6 (300) | 27 | 200 | 3.4 (7.5) |
0.045 in (1.1 mm) | 98% Ar / 2% O2 | DC+ | 20 (3/4) | 8.9 (350) | 28 | 225 | 3.9 (8.7) |
0.045 in (1.1 mm) | 98% Ar / 2% O2 | DC+ | 20 (3/4) | 10.2 (400) | 29 | 250 | 4.4 (9.8) |
1/16 in (1.6 mm) | 75% Ar / 25% CO2 | DC+ | 20 (3/4) | 3.8 (150) | 28 | 260 | 2.6 (5.8) |
1/16 in (1.6 mm) | 75% Ar / 25% CO2 | DC+ | 20 (3/4) | 6.4 (250) | 30 | 340 | 4.7 (10.4) |
1/16 in (1.6 mm) | 75% Ar / 25% CO2 | DC+ | 20 (3/4) | 8.9 (350) | 32 | 420 | 6.8 (15.1) |
1/16 in (1.6 mm) | 90% Ar / 10% CO2 | DC+ | 20 (3/4) | 3.8 (150) | 25 | 230 | 2.7 (6.0) |
1/16 in (1.6 mm) | 90% Ar / 10% CO2 | DC+ | 20 (3/4) | 6.4 (250) | 27 | 315 | 4.9 (10.7) |
1/16 in (1.6 mm) | 90% Ar / 10% CO2 | DC+ | 20 (3/4) | 8.9 (350) | 29 | 400 | 7.0 (15.4) |
1/16 in (1.6 mm) | 98% Ar / 2% O2 | DC+ | 20 (3/4) | 3.8 (150) | 24 | 220 | 2.9 (6.4) |
1/16 in (1.6 mm) | 98% Ar / 2% O2 | DC+ | 20 (3/4) | 6.4 (250) | 26 | 315 | 5.0 (11.0) |
1/16 in (1.6 mm) | 98% Ar / 2% O2 | DC+ | 20 (3/4) | 8.9 (350) | 28 | 410 | 7.1 (15.7) |
NOTES
Note |
---|
Interpass temperatures between 150°C (300°F) and 200°C (400°F) do not affect the hardness of Lincore® 55 significantly. |