Lincore® 15CrMn

Flux-Cored Self-Shielded (FCAW-S) | ED022061

CLASSIFICATIONS:
EN ISO : T Fe9

LINCORE® 15CRMN Flux-Cored Wire is ideal for austentic mangenese parts, can be used as a build-up overlay and for joining austenitic manganese steel to carbon steel, low alloy steel, austenitic manganese steel, or stainless steel (Severe Impact)

DETAILS

LINCOREĀ® 15CRMN Flux-Cored Wire provides good crack resistance, typical application includes Spreader cones, Crusher hammers and Austenitic manganese parts with proper preheat interpass temperatures for unlimited layers.

Features

  • Provides an austenitic manganese deposit which exhibits very good crack resistance
  • Work-hardens for overlay or joining austenitic manganese steel to itself or to carbon steel
  • Can be used as a build-up layer before capping with abrasion resistant alloys
  • Unlimited layers with proper preheat and interpass temperatures and procedures
  • Unlimited layers with proper preheat and interpass temperatures and procedures

Service Information

You May Also Need

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

MECHANICAL PROPERTIES

Classification Hardness Rockwell C
Typical Result 18-22
Typical Result, Work-hardened 45-50

DEPOSIT COMPOSITION

Classification %C %Cr %Mn %Si
Typical Result 0.4 16.0 15.0 0.2

TYPICAL OPERATING PROCEDURES

Diameter Polarity ESO
mm (in.)
Wire Feed Speed
m/min (in/min)
Voltage
volts
Approx. Current
amps
Deposition Rate
kg/hr (lb/hr)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 3.2 (125) 26 210 3.3 (7.3)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 5.1 (200) 29 280 5.3 (11.7)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 6.4 (250) 30 320 6.8 (15.1)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 8.9 (350) 32 380 9.7 (21.3)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 1.9 (75) 26 250 2.5 (5.5)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.2 (125) 28 320 5.1 (11.3)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.8 (150) 29 350 6.6 (14.6)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 4.4 (175) 30 380 7.5 (16.4)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 3.8 (150) 30 320 6.7 (14.9)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.1 (200) 33 390 8.7 (19.2)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.7 (225) 34 410 9.8 (21.7)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 6.4 (250) 35 425 11.4 (25.1)

NOTES

Note
As with all austenitic manganese welding products, interpass temperatures should be limited to 260°C (500°F) maximum.
A stringer bead, or at most, a slight weave is recommended to limit heat build-up. Excessive heat build-up causes manganese carbide precipitation that damages the toughness of austenitic manganese.