Détails
Ideal for building up on carbon and low alloy steels. Use as an underbase for carbon steel parts prior to hardfacing. Great compressive strength under heavy loading. Deposits are generally crack free, machinable and can be flame cut. Deposit thickness is unlimited. Used in Metal-to-Metal wear applications, works best in non-lubricated rolling or sliding.
Traits
- Can be use on low alloy steels
- Deposit is unlimited layers
- Can be used on work rolls and backup rolls when water spray causes pitting on tool steel deposits
- Metal-cored wire which produces a high carbon, 420 stainless steel deposit
- Use where a higher hardness is required
Disclaimers
Des informations de service
Vous pourriez également avoir besoin
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
MECHANICAL PROPERTIES
| Flux | Classification | Hardness Rockwell C |
|---|---|---|
| Lincolnweld® 801® | Typical Result | 48-54 |
DEPOSIT COMPOSITION
| Flux | Classification | %C | %Cr | %Mn | %Si |
|---|---|---|---|---|---|
| Lincolnweld® 801® | Typical Result | 0.23 | 13.0 | 1.2 | 0.4 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
|---|---|---|---|---|
| 3/32 in (2.4 mm) | DC+ | 1.7 (65) | 24 | 250 |
| 3/32 in (2.4 mm) | DC+ | 2.5 (100) | 28 | 525 |
| 3/32 in (2.4 mm) | DC+ | 4.4 (175) | 31 | 450 |
| 1/8 in (3.2 mm) | DC+ | 1.5 (60) | 26 | 360 |
| 1/8 in (3.2 mm) | DC+ | 2.5 (100) | 28 | 525 |
| 1/8 in (3.2 mm) | DC+ | 3.6 (140) | 30 | 635 |
| 5/32 in (4.0 mm) | DC+ | 1.4 (55) | 27 | 450 |
| 5/32 in (4.0 mm) | DC+ | 2.2 (85) | 30 | 650 |
| 5/32 in (4.0 mm) | DC+ | 2.9 (115) | 32 | 775 |