DETAILS
Ideal for building up on carbon and low alloy steels. Use as an underbase for carbon steel parts prior to hardfacing. Great compressive strength under heavy loading. Deposits are generally crack free, machinable and can be flame cut. Deposit thickness is unlimited.
Features
- Metal-cored wire for build-up on worn rolls
- A little softer than Lincore® 20 for easier machining
- Works great with Lincolnweld® 801® or Lincolnweld® 802®
Typical Applications
- Crane, Kiln
- Roll, Mine Car
- Shovel, Tractor
Welding Positions
- Flat/Horizontal
Special Features
- Used for 8620 type rolls
Disclaimers
Service Information
You May Also Need
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
MECHANICAL PROPERTIES
| Flux | Classification | Hardness Rockwell C |
|---|---|---|
| Lincolnweld® 801® | Typical Result | 16-20 |
DEPOSIT COMPOSITION
| Flux | Classification | %C | %Cr | %Mn | %Mo | %Ni | %Si |
|---|---|---|---|---|---|---|---|
| Lincolnweld® 801® | Typical Result | 0.09 | 0.45 | 0.80 | 0.15 | 0.55 | 0.30 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
|---|---|---|---|---|
| 1/8 in (3.2 mm) | DC+ | 1.5 (60) | 26 | 400 |
| 1/8 in (3.2 mm) | DC+ | 2.5 (100) | 28 | 550 |
| 1/8 in (3.2 mm) | DC+ | 3.6 (140) | 30 | 680 |